 Magnetic ceramic

Using microwave sintering gyromagnetic ferrite material, the whole material is heated, inside and outside temperature difference is small, quick temperature rise, and the microwave heating with "non-thermal" effects, can reduce the reaction temperature, crystals inside the object to promote densification. Sintered body of stress due to the small embryo, even if it does not result in the rate-determining embryo sintering cracking, and sintered materials have better performance, so that the passing rate of embryo sintering improved. Li et al., Microwave sintering method to produce permeability ui for Mn-Zn ferrite material 10000, the entire sintering cycle is a traditional 1/3 1/2, the properties of the materials meet or exceed the conventional sintering sample performance sintering method.